Applied Physics and Mathematics Annotation << Back CONCENTRATION BEHAVIOR OF LIQUIDUS TEMPERATURES AND UNDERCOOLING OF AL-CU-CO AT NORMAL PRESSURE L.V. KAMAEVA, YU.I. BRONNIKOVA, T.I. LATYPOV, A.I. GATAULLINA Differential thermal analysis has been conducted for the Al-Cu-Co alloys with the composition range of 15 at.% Co and 10 to 30 at.% Cu, and 25 at.% Co and 2.5 to 20 at.% Co. The features of the formation of solid phases have been studied during the crystallization in a crucible in the conditions of slow cooling (rate of cooling to 1 K s-1) at normal pressure. On the state diagram of the Al-Cu-Co system with 15 at.% Co and 25 at.% Cu the concentration sections have been built, which allows to determine the concentration ranges from which different phases are formed during the first stage of crystallization. Along the boundaries of different phase regions, extrema are observed on the liquidus line. The observed extrema on the liquidus lines and concentration dependences of undercooling are associated with change in the chemical short-range order at the considered concentrations both in the liquid and solid states. Keywords: undercooling; Al–Cu–Co alloys; Differential thermal analysis; Equilibrium state diagram. DOI: 10.25791/pfim.05.2023.1273 Pp. 03-09.